Plasters
PLASTER
1. MACHINE PLASTER
It is gypsum-based, ready-to-use spray plaster. It can be directly applied on brick, concrete, aerated-concerete, etc. It is a non-combustible material. The water in its structure helps retard fire. It has high surface hardness and a brilliant appearance. Because it is a breathable material, leads to a healthier environment by stabilizing humidity in the air.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 4 lt water to 10 kg |
Setting time starts | > 50 minutes (according to TS EN 13279-1) |
Setting time ends | ~ 180 minutes |
Consumption | ~ 10 kg/m² per 1 cm thickness |
Bulk density (powder) | ~ 850 kg/m³ |
Thermal conductivity | 0.43 W/m.K (According to TS EN 13279-1) |
Reaction to fire | A1 |
2. PRFMAX
Gypsum based concentreted machine plaster applied on concrete, brick, aerated concrete, hollow bricks etc. directly.
| TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
| Density | 550 – 700 kg/m² |
| Standard | TS EN 13279-1 |
| Reaction to fire | A1 |
3. HAND PLASTER
It is a gypsum- based, specially formulated ready-to-use bagged plaster that can be applied directly to brick, concrete, aerated concrete, etc. Its long workability time enables an easy application with a low waste rate.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 6,5 lt water to 10 kg |
Setting time starts | > 20 minutes (according to TS EN 13279-1) |
Setting time ends | ~ 150 minutes |
Consumption | ~ 8,5 kg/m² for each 1 cm thickness |
Bulk density (powder) | ~ 750 kg/m³ |
Thermal conductivity | 0.34 W/mK (According to TS EN 13279-1) |
Reaction to fire | A1 |
4. PRF25
PRF25 Hand Plaster, lightweight building plaster B4 (Hand applied). Gypsum based concentreted hand plaster applied on concrete, brick, aerated concrete, hollow bricks etc. directly.
5. SATIN PLASTER
It, with its high adherence, is a finishing plaster used as an undercoat for all types of painting. Its long workability time enables an easy application with a low waste rate. As it is a breathable material, by regulating humidity It leads to a healthier environment.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 6,5 – 7 lt water to 10 kg |
Setting time starts | > 20 minutes (according to TS EN 13279-1) |
Setting time ends | ~ 130 minutes |
Consumption | ~ 1 kg/m² for each 1 cm thickness |
Bulk density (powder) | ~ 750 – 800 kg/m³ |
Thermal conductivity | 0.34 W/mK (According to TS EN 13279-1) |
Reaction to fire | A1 |
6. PLASTER OF PARIS
It is a plaster used for the production of decorative elements like cornices. Its working time enables easy application with low wastage.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 6 – 7,5 lt water to 10 kg |
Setting time starts | > 8 minutes |
Setting time ends | ~ 130 minutes |
Compressive strength | 100 kgf/cm² (4×4 block) |
Bulk density (powder) | ~ 750 – 800 kg/m³ |
Reaction to fire | A1 |
7. JOINT FILLER PLASTER
It is a jointing compound which is used at plasterboard joints over joint tapes. Special additives in its structure retard the absorption of its moisture by the plasterboard surface.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 6 – 6,5 lt water to 10 kg |
Setting time starts | > 60 minutes |
Setting time ends | ~ 130 minutes |
Bulk density (powder) | ~ 750 – 800 kg/m³ |
Thermal conductivity | 0.39 W/mK |
Reaction to fire | A1 |
8. ADHESIVE PLASTERBOARD
It is a construction plaster that is used for bonding expanded polystyrene (EPS), extruded polystyrene (XPS), mineral wools (glasswool, rockwool) and composite insulation panels to surfaces such as brick, concrete, aerated concrete etc. It is the most convenient product for direct bonding applications where volume loss could be minimized by keeping wall as thin as possible.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | ~ 6,5 -7 lt water to 10 kg |
Setting time starts | > 45 minutes |
Setting time ends | ~ 80 minutes |
Bulk density (powder) | ~ 700 – 750 kg/m³ |
Thermal conductivity | 0.39 W/mK |
Reaction to fire | A1 |
9. SPECIAL PLASTER
9.1. ALFA
It is used in main molds, main models, porcelain lathe moulds, columns in buildings and decorations in forms that can be exposed to impacts, and in applications on floor slabs, which require strength especially with its alpha hard and tough molecular structure. It is a plaster used in pressure casting benches in the ceramic and porcelain industry. With its hard and durable structure, it provides the advantage of buying more products in a short time with the excess product taken from the molds with the air at 5 bar pressure applied with the air ducts laid inside.
TECHNICAL SPECIFICATIONS AND THE TSE STANDARD | |
Water / Plaster ratio | 38 – 42 |
Setting time starts | 3,5 – 10 minutes |
Setting time ends | 30 minutes |
9.2. RIGIPS – MULTIFIN
It has joint filling plaster and satin plaster properties. It has high adhesion strength and filling properties. In areas requiring 2-3 layers of satin plaster application, a single layer of MULTIFIN is sufficient. In areas where a mixture of perlite plaster and satin plaster is required, a single coat of MULTIFIN can be used. It has strong joint filling properties. Provides smooth top coat surface quality. It is used for corner profile positioning and provides convenience in light band applications.
AREAS OF USAGE
It can be easily used on all indoor surfaces such as exposed concrete, black plaster, gypsum plaster, plasterboard, chipboard, osb, plywood and raw wood surfaces.
9.3. USG – SHEETROCK BRAND ALL PURPOSE JOINT COMPOUND
A versatile all purpose joint compound providing professional-grade performance. Sheetrock® Brand All Purpose Joint Compound combines single-package convenience with good taping and topping performance. Recommended for laminating and repairing cracks in interior plaster and masonry not subject to moisture, this compound features great open time and cold bond, and has smooth and slick properties. This joint compound has achieved GREENGUARD Gold Certification and qualifies as a low VOC emitting material.